Incaline® - 3 mm thickness

Tensile strength	at +/- 6 mm dikte: +/- 25 N/mm²	ASTM D 790
Flexural strength	at +/- 6 mm dikte: +/- 25 N/mm²	ASTM D 790
Impact resistance	Undamaged	NEN 5335
Compressive strength	+/- 44 N/mm²	NBN B 12-208
Adhesive strength	Min. 2 N/mm²	CUR 20, methode 1
E-modulus (L.T)	10 jaar +/- 900 N/mm²
Abrasion strength	168 milligram	ASTM D4060
Hardness	+/- 77 Shore D	ISO 868
Water absorption	2,7 +/- 0,4 %	ISO 2812-2
Water resistance	3,2 + 0,3 N:mm² (L) 3,6 + 0,4 N:mm² (G)	ISO 2812-2
Chemical resistance	no change (PH 3) no change (PH13)	ISO 2812-1
Operational temperature	80°C continuous (L) 125°C continuous (G)	-
Temp. resistance	-20°C tot +80°C
Aging test	Adhesion system exceeds cohesion of the subsoil

Dielectric tests on concrete slab with epoxy resin

Applied voltage	Epoxy resin 6mm		Epoxy resin 3mm
Applied voltage	Electrode 10x10cm	Electrode 25x25cm	Electrode 25x25cm
5kV -		0,65mA
10kV -	0,24mA	1,27mA	2,20mA
11kV -	0,30mA	1,44mA	2,62mA
12Kv -	0,40mA	1,57mA	2,72mA
13kV -	0,43mA	1,70mA	3,00mA
14kV -	0,50mA	1,84mA	3,35mA
15kV -	0,55mA	1,88mA	3,55mA
16kV -	0,60mA	2,20mA	3,90mA
17kV -	0,66mA	2,38mA	4,20mA
18kV -	0,73mA	2,55mA	4,50mA
19kV -	0,80mA	2,75mA	4,80mA
20kV -	0,88mA	2,90mA	5,10mA
21kV -	0,95mA	3,10mA	(**)
22kV -	1,02mA	3,30mA
23kV -	1,10mA	3,50mA
24kV -	1,20mA	3,70mA
25kV -	1,28mA	4,30mA
26kV -	1,35mA	(*)
27kV -	1,45mA
28kV -	1,55mA
29kV -	1,65mA
30kV -	1,75mA
31kV -	1,85mA
32kV -	1,95mA
33kV -	2,05mA
34kV -	2,20mA
35Kv -	2,40mA
36kV -	(*)

(*) : flashover by surface conduction
(**) : flashover between electrode and concrete iron

Ask more info

Back to top

Vinylester

Physical and chemical characteristics of modified vinyl ester

Flexural modulus	3,6 GPa
Adhesion	Min. 1,5 N/mm² (crack concrete)
Impact resistance	> 13 KJ/m²
Chemical resistance	No chance (PH 3) No chance (PH 13)
Temperature resistance	-40°C tot +150°C
Barcol hardness	40
Stretch at breaking point	> 4%
Density	+/- 1,7 g/dm³

Ask more info

Back to top

Cementhoudende Coating 851

Cementitious modified polymer coating with exceptional waterpfoofing, anti-carbonation and chloride protection. Resisting positive and negative pressure under a 100 metre head.

Ask more info

Back to top

E 942

Two component, water based, epoxy and cementitious modified polymer coating for the protection of concrete and ferrous metals.

Ask more info

Back to top

E-Vloer

Epoxy and polymer modified cementitious coating with exceptional abrasion resistance and optional slip resistance.

Ask more info

Back to top

Curing Membrane

Non-degrading formulated acrylic resin sealer, which forms an elastic, durable matrix within cementitious substrates.

Ask more info

Back to top

2000-S

Tear resistant, breathable, waterproof composite tape, with a good UV resistance.
Impermeable to water under 10bar hydrostatic pressure.

Ask more info

Back to top

E-Primer

A modified, styrene acrylic copolymer impregnant with high penetration, which stabilises and seals cementitious and asphalt substrates.

Ask more info

Back to top

Elastische Coating

Cementitious modified, highly elastomeric, polymer-rich coating.

Ask more info

Back to top

Sandseal 760

A single pack, clear aliphatic polyurethane lacquer, dissolved in a hydrocarbon/ester solvent blend.

Can be applied to damp but surface dry substrates.

Moisture triggered curing mechanism rapidly gives a tough glossy finish.

Ask more info

Back to top

Fastfill

Rapid setting, high early strength hand placed repair mortar

Ask more info

Back to top

844 SP

Single component, thixotropic, polymer modified, cementitious repair mortar.

Ask more info

Back to top

Monolevel FC

A single component, thixotropic, polymer modified, cementitious mortar with high adhesive properties, allowing it to be used as a thin screed, as well as a filler, for filling minor voids and defects.

Ask more info

Back to top